Anisoprint Smooth PA Filament 1.75 mm, 750 cc

₹20029.00

Anisoprint Smooth PA Filament 1.75 mm, 750 cc
(0 reviews)
Product Features

• Low moisture absorption

• Anti-warping technology

• Excellent surface finish

• Reinforced with carbon fiber

- 23%
₹15338.00
MRP : ₹
20029.00
- +
Add to cart
Add to wishlist Remove from wishlist Compare Ask a question Share

Guarantee Safe Checkout:

  • card
  • card
  • card
  • card

Estimated delivery time: 4-5 business days

Free shipping on all orders

Frequently Bought Together
img-product
eSUN PLA+ 3D Printing Filament Fire Engine Red,1.75mm, Net Weight-1kg
₹1269.00 ₹2208.00
img-product
eSUN PLA+ 3D Printing Filament Orange,1.75mm, Net Weight-1kg
₹1269.00 ₹2208.00
img-product
eSUN ABS 3D Printing Filament White,1.75mm, Net Weight-1kg
₹1199.00 ₹1929.00
img-product
Creality ABS 3D Printing Filament Black ,1.75mm,Net Weight-1kg
₹1099.00 ₹1679.00
Total price:
₹60.00
Anisoprint Smooth PA Filament 1.75 mm, 750 cc
Add to cart
  • The Anisoprint Smooth PA is a carbon fiber-filled nylon developed by the Polymaker company specially for the use with the Anisoprint Composer A3 and A4 3D printers featuring the proprietary Anisoprint CFC (Continuous Fiber Co-extrusion) technology of printing with continuous fiber reinforced filaments.
  • The Composer printers are equipped with a dual extrusion system featuring a plastic and a composite extruder where composite carbon or basalt fiber is coated with a melted polymer matrix, and the reinforced filament goes through the nozzle to print a part.
  • The Smooth PA is a high performance easy-to-use filament which is great for printing strong durable functional models with a perfect surface finish. It is recommended to print at 250–270 °C using an abrasion-resistant nozzle, such as the Composer hardened steel nozzle (0.4 or 0.6 mm).
  • Low moisture absorption Anti-warping technology Excellent surface finish Reinforced with carbon fiber.
  • Tensile strength (X-Y) : 71.8 MPa
  • Young’s modulus (X-Y) : 5.82 GPa
  • Tensile strength (Z) : 15.2 MPa
  • Young’s modulus (Z) : 1.05 GPa
  • Bending strength (X-Y) : 109.97 MPa
  • Bending modulus (X-Y) : 3.54 GPa
  • Compressive strength (X-Y) : 81.4 MPa
  • Compressive modulus (X-Y) : 6.13 GPa
  • Elongation at break : 2.46%
  • HDT (0.45 MPa) : 131 °C
  • Notched Сharpy impact : 17.69 KJ/m²
Customer review
  • (0)
0.0 /5.0
5
0
4
0
3
0
2
0
1
0
Write a review
Write a review

Your email address will not be published. Required fields are marked *

Your rating *
Ask a Question
Your name*
Your phone number
Your email*
Message*
Provide Contact for Notification
Your name*
Your phone number
Your email*
Share
Copy